Stainless Steel 17-7PH

Short Introduction:

HY 17-7PH/S17700/SUS631/1.4568/AISI 631 is a precipitation hardenable stainless. It develops its strength and hardness through heat treating. This makes it well suited for applications that require good formability, high strength/hardness and minimum distortion upon heat treating. 17/7 also provides benefits for other applications requiring high strength and good corrosion resistance, as well as excellent properties for flat springs at temperatures up to 315°C (600°F).

    Category:

    Description

    Stainless Steel 17-7PH

    17/7PH alloy is a precipitation hardenable stainless. It develops its strength and hardness through heat treating. This makes it well suited for applications that require good formability, high strength/hardness and minimum distortion upon heat treating. 17/7 also provides benefits for other applications requiring high strength and good corrosion resistance, as well as excellent properties for flat springs at temperatures up to 315°C (600°F).
    17-7PH forgings, bars, plates, strips, rings, wires, flanges, etc. produced by Shanghai HY Industry Co., Ltd can be produced according to customer requirements, and are widely used in electric power, petrochemical, shipbuilding, machinery , Electronics, environmental protection and other industries.

    HY 17-7PH Material grades and equivalents

    UNS

    AISI/ASTM

    JIS

    W.Nr

    S17700

    631,17-7PH

    SUS631

    1.4568

    HY 17-7PH Chemical composition:

    C Mn P S Si Ch Ni Al Cr Fe
    Min  – 16.00 6.50 0.75 16 Bal
    Max 0.09 1.00 0.04 0.03 1.00 18.00 7.75 1.50 18

     

    HY 17-7PH Alloy minimum Mechanical properties in the room temperature:

    0.2% Proof Stress Tensile Strength Elongation Hardness
    MPA MPA % HRC
    Min 1035 1241 4 38
    Max 1448 6 46

     

    SPECIFIC GRAVITY

    7.81 g/cm3

    TYPICAL APPLICATIONS

    RELATED SPECIFICATIONS

    Chemical processing equipmentOil and Petroleum refining equipment

    Food processing equipment

    AMS 5528AMS 5529

    Mil S 25043

    UNS S17700