UNS C96400 pipe fittings are tested and ready for shipment
UNS C96400 pipe fittings are tested and ready for shipment
Notice of shipment goods:
Today, another batch of UNS C96400 pipe fittings has been tested and ready to be sent to the United States. Since this year, 15 batches have been successfully issued with a total value of more than 890,000 US dollars. Both in quality and delivery time are impeccable. Customers praise and increase mutual trust.
C96400 is the cast equivalent of 70/30 Cupro-Nickel. C964 shows good resistant to stress corrosion and is often used when an application will involve high-velocity seawater. UNS C96400 is often used in the production of fittings and flanges for shipboard application.
Common applications include:
Seawater applications
Valve components
Pump bodies
Chemical Composition
Cu%
Pb%
Fe%
P%
Ni%1
C%
Mn%
S%
Si%
Nb%
Chemical Composition according to ASTM B505/B505M-18
1Ni value includes Co.
Note: Cu + Sum of Named Elements, 99.5% min. Single values, unless otherwise noted, represent maximums.
Rem.
0.01
0.25-
1.50
0.02
28.00-
32.00
0.15
1.50
0.02
0.50
0.50-
1.50
Machinability
Copper Alloy UNS No.
Machinability Rating
Density (lb/in3 at 68 °F)
C96400
20
0.323
Mechanical Properties
Mechanical Properties according to ASTM B505/B505M-18
Tensile Strength, min
Yield Strength, at 0.5% Extension Under Load, min
Elongation, in 2 in. or 50 mm min
Brinell Hardness
Remarks
ksi
MPa
ksi
MPa
%
typical BHN
65
448
35
241
25
Physical Properties
US Customary
Metric
Physical Properties provided by CDA
Melting Point – Liquidus
2260 °F
1238 °C
Melting Point – Solidus
2140 °F
1171 °C
Density
0.323 lb/in3 at 68 °F
8.94 gm/cm3 at 20 °C
Specific Gravity
8.94
8.94
Electrical Conductivity
5% IACS at 68 °F
0.029 MegaSiemens/cm at 20 °C
Thermal Conductivity
16.4 Btu/sq ft/ft hr/°F at 68 °F
28.4 W/m at 20 °C
Coefficient of Thermal Expansion 68-572
9 · 10-6 per °F (68-572 °F)
15.5 · 10-6 per °C (20-300 °C)
Specific Heat Capacity
0.09 Btu/lb/°F at 68 °F
377.1 J/kg at 293 °C
Modulus of Elasticity in Tension
21000 ksi
144791 MPa
Fabrication Properties
Fabrication Properties provided by CDA
*Filler metal R CuNi, or E CuNi.
Technique
Suitability
Soldering
Excellent
Brazing
Excellent
Oxyacetylene Welding
Not Recommended
Gas Shielded Arc Welding*
Good
Coated Metal Arc Welding
Good
Machinability Rating
20
Specifications for C96400 Copper-Nickel
ASTM
Military
Centrifugal Cast
ASTM B369
MIL-C-20159
Sand Cast
ASTM B369
Continuous Cast
ASTM B505
Ingot
ASTM B30
HY-industry is qualified Nickelalloy&cobalt alloy materials supplier.
We have more than twenty years experience in kind of High temperature alloy production.
Inconel 718,Monel 400,Stellite 6，Stellite 12,Incoloy 800ht,Incoloy 901,Nimonic 80A,Kovar,Invar 36,Inconel 625,Hastelloy C276,Incoloy 825,UNS C96400 are mature productes of us.
When you want to know more about our products, please contact us: